Microstructural and crystallographic characteristics of interpenetrating and non-interpenetrating multiply twinned nanostructure in a Ni–Mn–Ga ferromagnetic shape memory alloy - Archive ouverte HAL Access content directly
Journal Articles Acta Materialia Year : 2011

Microstructural and crystallographic characteristics of interpenetrating and non-interpenetrating multiply twinned nanostructure in a Ni–Mn–Ga ferromagnetic shape memory alloy

(1, 2) , (1, 2) , (3) , (1, 2) , (4) , (1, 2) , (1, 2)
1
2
3
4

Abstract

A systematic investigation of microstructure and crystallography of the multiply twinned structure at the nanometer scale in a Ni 53 Mn 25 Ga 22 ferromagnetic shape memory alloy (FSMA) was performed. Nanoscale internal twins inside the micrometer-scale martensitic lamellae were observed. In each lamella, two nanotwin variants with a compound twinning relationship exist, and the twinning elements are K1 ={1 1 2}; K2 = {1 1 2}; n1 = {1 1 1}; n2 = {1 1 1}; P = {1 1 0} and s = 0:379. Two types of lamellar interfaces, i.e., interpenetrated interlamellar interface and stepped intralamellar interface, were revealed. The orientation relationships between the nanotwins connected by these two types of interfaces were unambiguously determined, and it was found that the respective orientation relationship between the neighboring nanotwins depends strongly on the adjacency condition at the interfaces. The possible formation mechanisms of the interpenetrated interlamellar interface and stepped intralamellar interface are discussed. These results are useful for property optimization by microstructure control in the FSMAs.
Fichier principal
Vignette du fichier
Microstructural and crystallographic characteristics of interpenetrating.pdf (1.43 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-03864499 , version 1 (26-12-2022)

Identifiers

Cite

D Y Cong, Y D Zhang, C Esling, Y D Wang, J.S. Lecomte, et al.. Microstructural and crystallographic characteristics of interpenetrating and non-interpenetrating multiply twinned nanostructure in a Ni–Mn–Ga ferromagnetic shape memory alloy. Acta Materialia, 2011, 59 (18), pp.7070 - 7081. ⟨10.1016/j.actamat.2011.07.062⟩. ⟨hal-03864499⟩
0 View
0 Download

Altmetric

Share

Gmail Facebook Twitter LinkedIn More