Engineering transformation pathways in an Al0.3CoFeNi complex concentrated alloy leads to excellent strength–ductility combination

Résumé

Guided by thermodynamic modeling, engineering phase transformation pathways via thermo-mechanical processing, in a complex concentrated alloy/high entropy alloy (HEA) of composition Al0.3CoFeNi, lead to a novel multi-scale microstructure consisting of fine-scale FCC + L12 grains mixed with B2 + BCC grains. The two-step pathway comprises initial decomposition of the parent single-phase FCC to form a fine-grained FCC + B2 microstructure, which further decomposes in the second step into the complex four-phase mixture, exhibiting an excellent combination of tensile yield stress of ∼1490 MPa, ultimate tensile strength of ∼1663 MPa, with a good ductility of ∼12% at room temperature.

Domaines

Matériaux
Fichier principal
Vignette du fichier
2020-098.pdf (3.28 Mo) Télécharger le fichier
Origine : Publication financée par une institution
Loading...

Dates et versions

hal-02908034 , version 1 (28-09-2020)

Identifiants

Citer

Sriswaroop Dasari, Abhinav Jagetia, Vishal Soni, Bharat Gwalani, S. Gorsse, et al.. Engineering transformation pathways in an Al0.3CoFeNi complex concentrated alloy leads to excellent strength–ductility combination. Materials Research Letters, 2020, 8 (11), pp.399-407. ⟨10.1080/21663831.2020.1777215⟩. ⟨hal-02908034⟩
54 Consultations
25 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More