Oxidation Resistance of Thermal Barrier Coatings Based on Hollow Alumina Particles

Abstract : Thermal barrier coatings were synthesized in a single step process from a slurry containing Al microspheres onto different Ni-based superalloys. Upon growth of the coating a top coat of hollow alumina spheres linked to an aluminium diffused coating through an alumina TGO formed. The isothermal and cyclic oxidation tests at different temperatures (900 till 1100°C) up to 1000h or 1500 cycles revealed progressive growth of different thermal oxides depending on the substrate composition. Faster degradation of the coatings occurred in the titanium-rich substrates (e.g. IN-738LC and PWA1483) compared to the titanium-poor ones (CM-247LC and René N5). By comparing with conventional low activity aluminide coatings, it appeared that the incorporation of alloying elements (notably Ti and Ta) to the diffused layers upon the high activity slurry coating process is responsible for such fastest degradation.
Complete list of metadatas

Cited literature [33 references]  Display  Hide  Download

https://hal.archives-ouvertes.fr/hal-02484849
Contributor : Fernando Pedraza <>
Submitted on : Wednesday, February 19, 2020 - 5:07:34 PM
Last modification on : Monday, March 30, 2020 - 3:34:22 PM

File

Pedraza_OXID MET_85_2016_231-2...
Files produced by the author(s)

Identifiers

Collections

Citation

F. Pedraza, M. Mollard, B. Rannou, B. Bouchaud, J. Balmain, et al.. Oxidation Resistance of Thermal Barrier Coatings Based on Hollow Alumina Particles. Oxidation of Metals, Springer Verlag, 2016, 85 (3-4), pp.231-244. ⟨10.1007/s11085-015-9570-3⟩. ⟨hal-02484849⟩

Share

Metrics

Record views

49

Files downloads

24