Stress partitioning in a near-β Titanium alloy induced by elastic and plastic phase anisotropies: experimental and modeling
Résumé
The load transfer induced by the elas c and plas c phase anisotropies of a Ti-10V-2Fe-3Al tanium alloy is studied. The microstructure consists in α nodules embedded in elongated β grains. EBSD performed on the alloy shows no crystallographic texture neither for α nor β phase. Tensile tests along the elonga on direc on, at a strain rate of 2 x 10-3 s-1 give a yield stress of 830 MPa with 13% duc lity. Simula ons based on an advanced two-phase polycrystalline elasto-viscoplas c self-consistent (EVPSC) model predict that the β phase first plas fies with a sequen al onset of plas city star ng from <110> oriented β grains, then <111> and finally <100> oriented β grains. This leads to a strong load transfer from the β grains to the α nodules whose average behavior remains elas c up to high stresses (~940 MPa). However, addi onal simula ons considering exclusively β grains of specific orienta on show that the behavior of α nodules is strongly dependent on the β texture in which they are embedded. Especially, in <001> β grains, which plas fy the latest, the model predicts the onset of plas city in favorably orientated α nodules. Moreover, the orienta on spread within the β grains can modify the average plas c behavior of α phase. In future, these results will be compared to data obtained from in-situ High Energy XRD and SEM/EBSD experiments.
Origine : Fichiers produits par l'(les) auteur(s)
Loading...